Masking flux for semiconductor components

ABSTRACT

A polymer masking flux for fabricating external contacts on semiconductor components includes a polymer resin, a fluxing agent and a curing agent. The flux is configured to clean contact pads for the external contacts, and to hold the external contacts on the contact pads during a reflow bonding process. The flux is also configured to cure or polymerize, to form donut shaped polymer support members for the external contacts. In addition, the flux is configured to mask conductive traces in electrical communication with the contact pads, and to electrically insulate the external contacts from the conductive traces. The external contacts can be pre-formed solder balls, or deposited solder bumps. In the case of solder bumps, the flux can include solder particles configured to coalesce into the solder bumps.

FIELD OF THE INVENTION

[0001] This invention relates generally to semiconductor packaging, and more particularly to a masking flux for fabricating external contacts, such as solder balls and solder bumps, on semiconductor components.

BACKGROUND OF THE INVENTION

[0002] Semiconductor components, such as packages, dice and wafers include external contacts which provide input/output paths to the integrated circuits contained on the components. For surface mount components, the external contacts typically comprise solder balls, or solder bumps, bonded to contact pads on the component. For some components, such as chip scale packages and BGA packages, the external contacts can be arranged in a dense grid array, such as a ball grid array (BGA), or a fine ball grid array (FBGA).

[0003] One conventional method for forming external contacts uses pre-formed solder balls, and a solder reflow bonding process. A prior art solder reflow bonding process is illustrated in FIGS. 1A-1D.

[0004] As shown in FIG. 1A, a semiconductor component 10 includes a pattern of contact pads 12 in electrical communication with the integrated circuits and semiconductor devices contained on the component 10. The contact pads 12 typically comprise a solder wettable metal such as chrome, titanium or nickel. The component 10 also includes a pattern of conductive traces 14 in electrical communication with the contact pads 12. In addition, the component 10 includes an electrically insulating solder mask 16 having openings 22 aligned with the contact pads 12. The solder mask 16 substantially covers the conductive traces 14, but as illustrated in FIG. 1A, the openings 22 sometimes expose portions of the conductive traces 14 that are in close proximity to the contact pads 12.

[0005] As shown in FIG. 1B, during the bonding process, a layer of flux 18 is deposited on the contact pads 12 using a suitable deposition process such as screen printing or pin transfer. The flux 18 chemically attacks surface oxides, such that the molten solder can wet the surfaces to be bonded. Typically, the flux comprises has either a rosin based or a water soluble chemistry.

[0006] As shown in FIG. 1C, following application of the flux 18, pre-formed solder balls 20 can be placed on the contact pads 12 in physical contact with the flux 18. Typically, the solder balls 20 have the shape of a sphere, or a truncated sphere. Although a fixture can be used to center and maintain the solder balls 20 on the contact pads 12, the flux 18 also performs a tacking function for holding the solder balls 20 on the contact pads 12 during the bonding process.

[0007] Following placement of the solder balls 20 on the contact pads 12, the component 10 can be placed in a furnace at a temperature sufficient to reflow and metallurgically bond the solder balls 20 to the contact pads 12. The component 10 can then be removed from the furnace and cooled. The component 10 can then be surface mounted to a supporting substrate, such as a printed circuit board, by bonding the solder balls 20 to corresponding electrodes on the supporting substrate.

[0008] In addition to reflowing the solder balls 20, the high temperatures encountered in the furnace can cause most of the flux 18 to vaporize in the furnace. However, a flux cleaning step is also required to remove any flux residue that remains on the contact pads 12 and component 10. The flux cleaning process can be performed using a hydrocarbon for a rosin based flux, or water with surfactants for a water soluble flux.

[0009] One factor that can adversely affect the reliability of the component 10 is shorting caused by distortion of the solder balls 20. As shown in FIG. 1D, distortion of the solder balls 20 can cause portions of the solder balls 20 to touch exposed portions of the conductive traces 14. It would be advantageous for a flux to be curable and electrically insulating, such that shorting between the solder balls 20 and the conductive traces 14 can be eliminated. Another factor that can affect the reliability of the component during normal operation is fatigue failure of the solder balls 20, particularly at the interfaces with the contact pads 12 and the electrodes on the supporting substrate. Typically, fatigue failures are induced by thermal expansion mismatches between the component and the supporting substrate. For example, if the component 10 comprises a first material, such as silicon having a first TCE (thermal coefficient of expansion), and the supporting substrate comprises a second material, such as FR-4 having a second TCE, cyclic forces can be placed on the solder balls 20 as the component 10 is thermally cycled during normal operation.

[0010] These forces can include tensile forces, moment forces and shear forces. If the forces are large enough, the solder balls 20 can separate from the contact pads 12 forming an electrical open. The separation can also compromise the physical bond between the component 10 and the supporting substrate. This problem is compounded because the area of interface between the solder balls 20 and the contact pads 12 is relatively small, such that the forces are concentrated over a relatively small area.

[0011] It would be advantageous for a flux to have the capability to support and rigidify the solder balls 20, or other external contacts, on a semiconductor component 10, during normal operation of the component 10. The present invention is directed to an improved flux configured to form a rigidifying structure for the external contacts. In addition, the flux is formulated to remove oxides from the components, is curable for reducing vapors during the fabrication process, and is electrically insulating for masking conductive traces for the external contacts.

SUMMARY OF THE INVENTION

[0012] In accordance with the present invention, an improved polymer masking flux for fabricating external contacts on semiconductor components, a bonding system that includes the flux, and improved components fabricated using the flux, are provided.

[0013] In an illustrative embodiment the component comprises a semiconductor package, a semiconductor die, or a semiconductor wafer, and the external contacts comprise solder balls. The component includes a substrate, contact pads on the substrate and conductive traces in electrical communication with the contact pads. The component also includes a solder mask having openings aligned with the contact pads.

[0014] The flux is configured to clean surface oxides from the contact pads during reflow bonding of the solder balls to the contact pads. In addition, the flux masks exposed portions of the conductive traces, and prevents electrical shorting between the solder balls and the conductive traces. The flux is also configured to cure, or polymerize, in a reflow furnace, and form polymer support members for the solder balls. The polymer support members are donut shaped elements that rigidify, and absorb forces acting on the solder balls during subsequent use of the component. Each polymer support member surrounds a base portion of a solder ball, and has a thickness approximately equal to one tenth to one half the diameter of the solder balls.

[0015] The flux includes an electrically insulating polymer resin such as an epoxy resin, a silicone resin, natural rubber or synthetic rubber. The polymer resin provides a base material which cures or polymerizes into the polymer support members. In addition, the flux includes a fluxing agent, such as an organic acid, for cleaning and removing oxides from the surface of the contact pads and the solder balls. The flux also includes a curing agent or hardener, such as a reactant or a solvent, that reacts with and cures the polymer resin in the reflow furnace. Because the flux cures into the polymer support members, vapors in the reflow furnace are reduced, and there is no need to perform a flux cleaning step on the component following the reflow bonding process.

[0016] The flux is a relatively thick viscous material that has non-flowing characteristics over a selected temperature range. This allows an exact quantity of the flux to be deposited onto the contact pads as a droplet using pin transfer, nozzle deposition or screen printing processes. The droplet maintains it's shape, remains on the contact pads, and provides high adhesion for tacking the solder balls to the contact pads during the reflow bonding step. The flux can be used at the wafer level during the fabrication of multiple components at the same time (i.e., wafer level fabrication process), or can be employed on singulated components such as individual dice or packages (i.e., die level fabrication process).

[0017] A system for bonding the solder balls to the semiconductor component includes the flux, and a flux dispensing mechanism configured to deposit the droplets of flux onto the contact pads. The system also includes a conveyor, a ball placement mechanism and a reflow furnace.

[0018] The flux can also be used to fabricate external contacts in the form of solder bumps, rather than solder balls. In this case the flux again includes the polymer resin, the fluxing agent, and the curing agent. The flux also includes micro solder particles configured to coalesce into the solder bumps. The flux is initially deposited onto the contact pads using a deposition process, such as screen printing, or nozzle deposition. The polymer resin masks exposed portions of the conductive traces, and the fluxing agent cleans surface oxides from the contact pads. Following deposition, the flux is reflowed by heating the components in a reflow furnace. During the reflow step, the solder particles and the polymer resin separate, such that the solder particles form the solder bumps, and the polymer resin forms polymer support members for the solder bumps.

BRIEF DESCRIPTION OF THE DRAWINGS

[0019] FIGS. 1A-1D are schematic cross sectional views illustrating a prior art reflow bonding process for solder balls;

[0020] FIGS. 2A-2D are schematic cross sectional views illustrating a reflow bonding process performed using a preformed solder ball and a flux formulated in accordance with the invention;

[0021]FIG. 3A is a cross sectional view taken along section line 3A-3A of FIG. 2A;

[0022]FIG. 3B is a cross sectional view taken along section line 3B-3B of FIG. 2B;

[0023]FIG. 3C is a cross sectional view taken along section line 3C-3C of FIG. 2C;

[0024]FIG. 3D is a cross sectional view taken along section line 3D-3D of FIG. 2D;

[0025] FIGS. 4A-4C are schematic cross sectional views illustrating a reflow bonding process performed using a polymer flux fabricated in accordance with an alternate embodiment of the invention;

[0026]FIG. 5A is a schematic illustration of a system constructed in accordance with the invention for bonding external contacts to semiconductor components; and

[0027]FIG. 5B is a plan view taken along line 5B-5B of FIG. 5A illustrating the component prior to bonding of the external contacts.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

[0028] As used herein, the term “semiconductor component” means an electronic component that includes a semiconductor die. Exemplary semiconductor components include bare semiconductor dice, chip scale packages, ceramic or plastic semiconductor packages, BGA devices, semiconductor wafers, and panels and leadframes containing multiple dice or chip scale packages.

[0029] Referring to FIGS. 2A-2D, and FIGS. 3A-3D, a process for fabricating external contacts on a semiconductor component 28 using a polymer flux formulated in accordance with the invention is illustrated.

[0030] As shown in FIGS. 2A and 3A, the semiconductor component 28 is provided, and includes a substrate 30. The substrate 30 can be provided as a wafer, a panel, or a leadframe, containing a plurality of components 28 that can be singulated following the fabrication process (i.e., wafer level process). Alternately, the component 28 and the substrate 30 can comprise a singulated element, such as an individual package or die. Depending on the component 28, the substrate 30 can comprise a semiconductor material, such as silicon, or a plastic material, such as bismaleimide triazine (BT), or a polyimide resin.

[0031] The substrate 30 includes a surface 31, and a contact pad 32 on the surface 31. For simplicity only one contact pad 32 is shown. However, the substrate 30 includes a plurality of contact pads 32 arranged in a desired pattern such as a dense grid array. The contact pad 32 comprises a solder wettable material such as copper, tin, lead, palladium, platinum, nickel, chrome, titanium or gold.

[0032] The substrate 30 also includes a conductive trace 36 (FIG. 3A) in electrical communication with the contact pad 32. The conductive trace 36 establishes electrical communication between the contact pad 32 and the integrated circuits contained on the component 28. The substrate 30 also includes a conductive trace 34 in electrical communication with another contact pad that is not illustrated. The conductive traces 34, 36 comprise a highly conductive material such as aluminum, titanium, nickel, iridium, copper, gold, tungsten, silver, platinum, palladium, tantalum, molybdenum or alloys of these metals.

[0033] The substrate 30 also includes a mask 38 having an opening 40 aligned with the contact pad 32. The mask 38 comprises an electrically insulating material, such as a photoimageable resist. The mask 38 electrically insulates the conductive traces 34, 36 and prevents shorting between the contact pad 32 and adjacent contact pads. As shown in FIG. 3A, in addition to exposing the contact pad 32, the opening 40 in the mask 38 also exposes portions of the conductive traces 34, 36.

[0034] Next, as shown in FIGS. 2B and 3B, a flux deposition step is performed in which a droplet 42 of polymer masking flux is deposited through the opening 40 in the mask 38 onto the contact pad 32. Again, although only a single droplet 42 of flux is illustrated, it is understood that the component 28 will include as many droplets as there are contact pads 32, but only one droplet 42 per contact pad 32. In the illustrative embodiment, the droplet 42 covers the contact pad 32, completely fills the opening 40, and covers the exposed portions of the conductive traces 34, 36. The size of the droplet 42 will depend on the size of the contact pad 32 and the opening 40. In addition, the droplet 42 has a generally dome shaped topography with a convex surface. The droplet 42 can be deposited on the contact pad 32 using a suitable deposition process, such as pin transfer, positive displacement through a nozzle, or screen printing. A suitable pin transfer mechanism is included in a ball placement system manufactured by Motorola of Phoenix, Ariz. as a model no. MS250PLUS. A suitable positive displacement mechanism is a “MICRO PEN” manufactured by Ohmcraft Inc. of Pittsford, N.Y. Another suitable positive displacement mechanism is a “2800” liquid dispensing system manufactured by Camelot Systems, Inc. of Haverhill, Mass. With screen printing a stainless steel or monofilament polyester screen can be stretched and attached to a metal frame. A negative pattern can then be generated on the mesh using a photosensitive emulsion. The flux can then be forced through screen and onto the contact pad 32.

[0035] The polymer masking flux is formulated to meet environmental standards recognized in the semiconductor industry. In addition, the polymer masking flux is formulated with a viscosity that allows the droplet 42 to have non-flowing characteristics at a selected temperature range, such as room temperature (e.g., 60° F. to 100° F. or 15.5° C. to 37.8° C.). This viscosity allows the polymer masking flux to maintain a desired size and shape, and to remain in a desired area of the substrate 30 over the temperature range. By way of example, the polymer masking flux can have a viscosity at a temperature of about 25° C. of about 100 to 1500 poise. In this case the viscosity can be measured using a spiral/Malcom viscometer at 25 rpm,

[0036] As a primary constituent the polymer masking flux includes an electrically insulating polymer resin such as an epoxy resin, a silicone resin, natural rubber, synthetic rubber, or similar elastomeric material having suitable non-flowing and curable properties. By way of example, specific polymer resins include, but are not limited to: pthalate-actate acetate hydroxyl copolymer, dibutyl isobutyl diphenol cellulose copolymer, and butyl phenol ketyl vinyl acetate polymer.

[0037] The polymer masking flux also includes a fluxing agent, such as an organic acid, for cleaning and removing oxides from the surface of the contact pads 42 and the solder balls 44. Suitable fluxing agents include carboxylic acid, abietic acid, citric acid, 2-furoic acid, malic acid and polyacrylic acid. A representative proportion of the fluxing agent as a volume percentage of the total volume of the droplet 42 can be from about 0.1% to 16%.

[0038] The polymer masking flux also includes a curing agent or hardener, such as a reactant or a solvent, that reacts with and cures the polymer resin over a selected temperature range and time period. Suitable curing agents include amines, anhydrides, and butyl carbitol acetate. The fluxing agent and the curing agent can also comprise a same chemical compound. By way of example, the curing agent can be included in the polymer resin in a quantity sufficient to cure the polymer resin at a temperature of between about 200° C. to 250° C. in about 1 to 2 minutes. The curing process can be performed simultaneous with a reflow step using a reflow furnace to be hereinafter described. If required, a final cure can also be performed at a lower temperature for a longer time period. In this case a batch oven can be used to perform the final cure.

[0039] As shown in FIG. 2C and FIG. 3C, following the droplet deposition step, a ball placement step is performed in which a solder ball 44 is placed on the droplet 42, and pushed into contact with the contact pad 32. Preferably, the ball placement step is performed at room temperature such that the viscous properties of the droplet 42 are maintained. In this viscous condition, the droplet 42 also has adhesive properties that hold the solder ball 44 on the contact pad 32 with an adhesive force. The ball placement step must be performed with sufficient force to permit the solder ball 44 to displace the middle portion of the droplet 42, and physically contact the contact pad 32.

[0040] The solder ball 44 can be formed separately out of a suitable solder alloy, such as 95%Pb/5%Sn, 60%Pb/40%Sn, 63%Sn/37%Pb, or 62%Pb/36%Sn/2%Ag. A representative range for the outside diameter (OD) of the solder ball 44 can be from about 0.002-in (0.050 mm) to 0.025-in (0.675 mm). A representative thickness T of the droplet 42, with the solder ball 44 in contact with the contact pad 32, can be from about one tenth to one half the outside diameter of the solder ball 44.

[0041] The solder ball 44 can be pushed through the droplet 42, and placed on the contact pad 32 using a suitable ball placement mechanism. Such a ball placement mechanism is included in the previously identified ball placement system MS250PLUS manufactured by Motorola. Another ball placement mechanism suitable is disclosed in U.S. Pat. No. 6,100,175 to Wood et al. entitled “Method And Apparatus For Attaching Balls To A Substrate”.

[0042] Next, as shown in FIG. 2D and FIG. 3D, a heating or reflow step is performed in which the component 28 is placed in a furnace, and the solder ball 44 is heated to a temperature sufficient to reflow the solder. During the heating step, the reflowed solder ball 44 metallurgically bonds to the contact pad 32. Also during the heating step, the droplet 42 of flux polymerizes, or cures, into a polymer support member 46.

[0043] As shown in FIG. 3D, the polymer support member 46 is a donut shaped structure (torus) resting on the surface 31 of the substrate 30, and encompassing the base portion of the solder ball 44. The polymer support member 46 helps to support and rigidify the solder ball 44 during subsequent operation of the component 28. In this regard, the polymer support member 46 bonds to the solder ball 44, bonds to the opening 40 in the mask 38, and bonds to the surface of the mask 38 to provide a rigidifying structure anchored to the substrate 30.

[0044] In addition to performing a supporting and rigidifying function, the polymer support member 46 also performs a masking and electrical insulating function. Specifically, the polymer support member 46 masks the exposed portions of the conductive trace 34, and prevents shorting between the solder ball 44 and the conductive trace 34. In addition, the polymer support member 46 provides an electrically insulating material in the opening 40, and between the solder ball 44 and the conductive trace 34.

[0045] Referring to FIGS. 4A-4C, a process for fabricating solder bumps 48 (FIG. 4C) using the polymer masking flux are illustrated. Initially, as shown in FIG. 4A, the component 28 is provided and includes the substrate 30, the contact pad 32, the conductive trace 34, the mask 38, and the opening 40 in the mask 38, substantially as previously described.

[0046] As also shown in FIG. 4A, a deposition apparatus 52 is provided. The deposition apparatus is configured to deposit a polymer masking flux 50 on the contact pad 32. The polymer masking flux 50 includes a polymer resin formulated with the previously described characteristics, a fluxing agent for cleaning the contact pad 32 and a curing agent for curing the polymer resin. The polymer masking flux 50 also includes solder particles having a desired particle size distribution.

[0047] In the illustrative embodiment, the deposition apparatus 52 comprises a screen printer comprising a screen 54 having an opening 58, and a squeegee 56 configured to push the polymer flux 50 through the opening 58 onto the contact pad 32. Alternately, the deposition apparatus can comprise a positive displacement mechanism as previously described, configured to dispense the polymer masking flux 50 under pressure through a nozzle.

[0048] Next, as shown in FIG. 4B, a flux deposition step is performed. During this step, the squeegee 56 is used to force the polymer masking flux 50 through the opening 58 in the screen 54, and onto the contact pad 32, to form a droplet 60 of flux. During the deposition step the polymer masking flux 50, and the droplet 60, are viscous, uncured, and non-flowing substantially as previously described. In addition, the droplet 60 has a peripheral shape corresponding to the peripheral shape of the opening 58 (e.g., circular, square, rectangular). The droplet 60 has a height corresponding to the height of the screen 54 above the contact pad 32.

[0049] Next, as shown in FIG. 4C, a reflow bonding step is performed in a furnace substantially as previously described. During the reflow bonding step the droplet 60 of polymer masking flux 50 is heated to a temperature sufficient to coalesce the solder particles therein into a generally hemispherically shaped solder bump 48. In addition, during the reflow bonding step the polymer resin separates from the solder particles, moves outward, and polymerizes into the polymer support member 46.

[0050] Also during the reflow bonding step, the polymer resin in the droplet 60 masks and electrically insulates the conductive trace 34, substantially as previously described. As before, the curing mechanism can comprise outgassing of a solvent during heating as indicated by vapor trails 76. As also previously described, curing can be accomplished in a first stage at a relatively high temperature (e.g., 250° C.) for a relatively brief time (e.g., 1 minute), followed by a second stage at a lower temperature (e.g., 100° C. for a longer time (e.g., several minutes or more).

[0051] Referring to FIGS. 5A and 5B, a system 62 for bonding the solder balls 44 to the component 28 is illustrated schematically. The system 62 includes a conveyor 64 for moving the component 28 through the different stages of the system 62. The conveyor 28 includes lugs 66 for engaging the component 28. For example, the component 28 can be mounted to a leadframe or a panel having openings configured to engage the lugs 66. As shown in FIG. 5B, the component 28 includes the contact pads 32 formed substantially as previously described. In the illustrative embodiment, the contact pads 32 are generally circular in shape, and are arranged in a dense grid array of rows and columns.

[0052] As also shown in FIG. 5A, the system 62 includes a flux dispensing mechanism 68 configured to dispense a viscous polymer masking flux 70, formulated as previously described, onto the contact pads 32 to form the droplets 42. The flux dispensing mechanism 68 can comprise a pin transfer mechanism, a positive displacement mechanism having one or more nozzles, or a screen printing apparatus, all as previously described.

[0053] As also shown in FIG. 5A, the system 62 includes a ball placement mechanism 72 configured to place the solder balls 44 on the droplets 42 in physical contact with the contact pads 32 substantially as previously described. The system 62 also includes a two stage furnace 74 configured to reflow the solder balls 44, and to cure the droplets 42 to form the polymer support members 46 substantially as previously described. Suitable furnaces are available from Scientific Sealing Technology of Downey, Calif., Vitronics of New Hampshire, and Accel of Texas.

[0054] Thus the invention provides an improved polymer masking flux for fabricating external contacts on semiconductor components, a system for fabricating external contacts that includes the polymer flux, and improved semiconductor components fabricated using the polymer flux. While the invention has been described with reference to certain preferred embodiments, as will be apparent to those skilled in the art, certain changes and modifications can be made without departing from the scope of the invention as defined by the following claims. 

What is claimed is:
 1. A flux for fabricating an external contact on a semiconductor component having a contact pad comprising: an electrically insulating polymer resin configured for deposition on the contact pad as a viscous non-flowing droplet that electrically insulates at least a portion of the external contact; a fluxing agent in the polymer resin configured to clean the contact pad; and a curing agent in the polymer resin configured to cure the polymer resin into a polymer support member for the external contact.
 2. The flux of claim 1 wherein the polymer resin comprises a material selected from the group consisting of epoxy, silicone and rubber.
 3. The flux of claim 1 wherein the fluxing agent comprises an acid and the curing agent comprises a solvent.
 4. The flux of claim 1 wherein the fluxing agent and the curing agent comprises a same chemical compound.
 5. The flux of claim 1 wherein the external contact comprises a solder ball placed on the droplet and the polymer support member comprises a donut shaped element.
 6. The flux of claim 1 wherein the flux comprises a plurality of solder particles configured to form the external contact as a solder bump.
 7. The flux of claim 1 wherein the component comprises a conductive trace and the flux is configured to mask at least a portion of the trace.
 8. A flux for fabricating an external contact on a semiconductor component having a contact pad and a conductive trace proximate to the contact pad comprising: an electrically insulating polymer resin configured for deposition onto the contact pad as a non-flowing viscous droplet configured to mask at least a portion of the conductive trace; a fluxing agent in the polymer resin configured to clean the contact pad; and a curing agent in the polymer resin configured to cure the polymer resin into a polymer support member attached to and rigidifying the external contact.
 9. The flux of claim 8 wherein the droplet has a viscosity of about 100 to 1500 poise at a temperature of about 25° C.
 10. The flux of claim 8 wherein the external contact comprises a solder ball and the droplet is configured to adhere the solder ball to the contact pad.
 11. The flux of claim 8 further comprising a plurality of solder particles configured to form the external contact.
 12. The flux of claim 8 wherein the polymer resin comprises a material selected from the group consisting of epoxy, silicone and rubber.
 13. The flux of claim 8 wherein the fluxing agent comprises an acid.
 14. The flux of claim 8 wherein the curing agent comprises a solvent or a reactant.
 15. The flux of claim 8 wherein the curing agent is configured to at least partially cure the polymer resin at a temperature of about 200° C. to 250° C.
 16. The flux of claim 8 wherein the component comprises a semiconductor package.
 17. The flux of claim 8 wherein the component comprises a semiconductor die or a semiconductor wafer.
 18. A flux for bonding an external contact to a contact on a semiconductor component comprising: a polymer resin comprising a material selected from the class consisting of epoxy, silicone and rubber configured for deposition on the contact as a viscous non-flowing droplet able to support and electrically insulate the external contact on the contact; a fluxing agent in the polymer resin configured to clean the contact; and a curing agent in the polymer resin configured to cure the polymer resin on the contact into a polymer support member for the external contact.
 19. The flux of claim 18 wherein the external contact comprises a solder ball.
 20. The flux of claim 18 wherein the external contact comprises a solder bump.
 21. The flux of claim 18 wherein the component comprises a semiconductor package, a semiconductor wafer or a semiconductor die.
 22. The flux of claim 18 wherein the fluxing agent and the curing agent comprise a same chemical compound.
 23. The flux of claim 18 wherein the droplet has a thickness of about one tenth to one half a diameter of the external contact.
 24. A flux for bonding a solder ball to a contact pad on a semiconductor component comprising: an electrically insulating polymer base material depositable on the contact pad at room temperature as a viscous non-flowing droplet configured to support the solder ball on the contact pad and to electrically insulate at least a portion of the solder ball; a fluxing agent in the polymer base material configured to clean the contact pad; and a curing agent in the polymer base material configured to cure the polymer base material into a support member on the component configured to support and rigidify the solder ball following bonding to the contact pad.
 25. The flux of claim 24 wherein the polymer base material comprises a material selected from the class consisting of epoxy, silicone and rubber.
 26. The flux of claim 24 wherein the curing agent comprises a solvent or a reactant and the fluxing agent comprises an acid.
 27. The flux of claim 24 wherein the curing agent and the fluxing agent comprise a same chemical compound.
 28. The flux of claim 24 wherein the droplet has a thickness on the contact pad of from one tenth to one half a diameter of the solder ball.
 29. The flux of claim 24 wherein the component comprises a semiconductor package, a semiconductor wafer or a semiconductor die.
 30. A flux for fabricating an external contact on a semiconductor component having a contact pad and a conductive trace proximate to the contact pad comprising: an electrically insulating polymer resin formulated for deposition onto the contact pad as a non-flowing viscous droplet configured to mask at least a portion of the conductive trace; a plurality of solder particles in the polymer resin configured to coalesce to form the external contact; a fluxing agent in the polymer resin configured to clean the contact pad; and a curing agent in the polymer resin configured to cure the polymer resin into a polymer support member attached to and rigidifying the external contact.
 31. The flux of claim 30 wherein the droplet has a viscosity of about 100 to 1500 poise at a temperature of about 25° C.
 32. A system for bonding external contacts to contact pads on semiconductor components: a polymer flux; and a flux dispensing mechanism configured to deposit the flux onto the contact pads; the polymer flux comprising a polymer resin configured for deposition by the mechanism on the contact pads as a viscous non-flowing droplet able to support and electrically insulate the external contacts on the contact pads for bonding, a fluxing agent in the polymer resin configured to clean the contact pads; and a curing agent in the polymer resin configured to cure the polymer resin on the contact pads into a polymer support member for the external contact.
 33. The system of claim 32 further comprising a placement mechanism configured to place the external contacts on the droplets and contact pads.
 34. The system of claim 32 further comprising a furnace configured to reflow bond the external contacts to the contact pads and to heat the polymer flux for curing.
 35. The system of claim 32 wherein the external contacts comprise solder balls.
 36. The system of claim 32 wherein the polymer resin comprises a material selected from the class consisting of epoxy, silicone and rubber.
 37. The system of claim 32 wherein the curing agent comprises a solvent or a reactant and the fluxing agent comprises an acid.
 38. The system of claim 32 wherein the curing agent and the fluxing agent comprise a same chemical compound.
 39. The system of claim 32 wherein the droplet has a thickness on the contact pad of from one tenth to one half a diameter of the solder ball.
 40. The system of claim 32 wherein the component comprises a semiconductor package, a semiconductor wafer or a semiconductor die.
 41. A system for fabricating an external contact on a semiconductor component having a contact pad comprising: an electrically insulating polymer flux comprising a polymer resin, a plurality of solder particles in the polymer resin configured to coalesce into a solder bump, a fluxing agent in the polymer resin configured to clean the contact pad, and a curing agent in the polymer resin configure to cure the polymer resin into a polymer support member for the solder bump, the polymer flux having a viscosity at room temperature that permits deposition as a viscous non-flowing droplet; a flux dispensing mechanism configured to deposit the droplet on the contact pad; and a furnace configured to heat the polymer resin and the solder particles to a temperature sufficient to bond the solder particles to the contact pad and to cure the polymer resin into the polymer support member.
 42. The system of claim 41 wherein the flux dispensing mechanism comprises a screen printing mechanism.
 43. The system of claim 41 wherein the component comprises a package, a die, or a wafer.
 44. The system of claim 41 further comprising a conveyor configured to move the component.
 45. The system of claim 41 wherein the fluxing agent comprises an acid and the curing agent comprising a solvent.
 46. A system for bonding an external contact to a contact pad on a semiconductor component: a solder ball; a polymer flux configured for deposition on the contact as a droplet of flux that supports the solder ball for bonding to the contact pad and electrically insulates at least a portion of the external contact, the polymer flux comprising a polymer resin curable on the contact pad to form a polymer support member for the solder ball, a fluxing agent in the polymer resin configured to clean the contact pad, and a curing agent in the polymer resin configured to cure the polymer resin into the polymer support member; a flux dispensing mechanism configured to dispense the droplet of flux on the contact pad; and a furnace configured to heat the polymer flux and the solder ball to a temperature sufficient to cure the polymer flux and to bond the solder ball to the contact pad.
 47. The system of claim 46 further comprising a placement mechanism configured to place the solder ball on the contact pad.
 48. The system of claim 46 wherein the polymer resin comprises a material selected from the class consisting of epoxy, silicone and rubber.
 49. The system of claim 46 wherein the curing agent comprises a solvent or a reactant.
 50. The system of claim 46 wherein the fluxing agent comprises an acid.
 51. The system of claim 46 wherein the droplet has a thickness on the contact pad of from one tenth to one half a diameter of the solder ball.
 52. The system of claim 46 wherein the component comprises a semiconductor package, a semiconductor wafer or a semiconductor die. 